TY - JOUR ID - 20884 TI - Fabrication of Crosslinkable Hollow Fiber Membranes for Pervaporation Dehydration JO - Journal of Membrane Science and Research JA - JMSR LA - en SN - AU - Ge, Li AU - Ying, Jiang Lan AD - Central South University Y1 - 2017 PY - 2017 VL - 3 IS - 4 SP - 281 EP - 290 KW - Pervaporation KW - PEI KW - PVA KW - Integrated asymmetric membrane KW - crosslinking DO - 10.22079/jmsr.2016.20884 N2 - Integrally-skinned asymmetric Polyetherimide/Poly (vinyl alcohol) (PEI/PVA) hollow fber membranes for pervaporation dehydration were fabricated by non-solvent induced phase inversion. PVA inside the PEI matrix could be crosslinked to provide membrane performance stability during long term operation. The effects of different PEI/PVA blend ratio, external coagulant type and flow rate, and crosslinking conditions on the membrane structure and the separation performance were investigated. Generally, hollow fbers using PEI/PVA blend are less selective than those of neat PEI, probably due to the defects evolved between PEI and PVA. The influence of coagulant type on membrane pervaporation performance was specifc to dope formulation; when using n-butanol as external coagulant, the higher the coagulant flow rate, the better the membrane separation performance. PVA crosslinking by maleic acid (MA) enhanced the membrane performance, obviously. PEI/PVA Hollow fbers formed using n-butanol as external coagulant obtained a separation factor of 28 after crosslinking, much better than 4.4 with the original one. The crosslinked membrane exhibited higher stability than the neat PEI membrane. The separation factor of the latter degraded by more than half after around 200 h operation. Finally, this work has provided a new approach for fabricating crosslinkable asymmetric membrane suitable for pervaporation dehydratio. UR - https://www.msrjournal.com/article_20884.html L1 - https://www.msrjournal.com/article_20884_94e1a5cf53d4125c15a672bf8f96b8e3.pdf ER -